From titanium bone regeneration scaffolds and hydraulic components to nuclear components and flow reactors, selective laser melting (SLM), which is also known as DMLS and Powder Bed Fusion, is an especially helpful method of metal 3D printing. But there are still some challenges to face before SLM is a true mainstream manufacturing process, such as process repeatability and the fact that so much time-consuming, costly post-processing is often needed for a part to be viable. The surface quality of 3D printed parts fresh off the bed can leave much to be desired.
A collaborative group of researchers from the Karlsruhe Institute of Technology (KIT), Port Said University in Egypt, and 3D Systems recently published a paper, titled “A Study of the Factors Influencing Generated Surface Roughness of Down-facing Surfaces in Selective Laser Melting,” on their investigation of the effects of different process parameters on the surface roughness of 3D printed down-facing surfaces.
The abstract reads, “The aim of this work is to investigate the effect of varying process parameters on the resultant roughness of the down-facing surfaces. The results indicate that the Sz parameter provides greater insight into the quality of down-facing surfaces than the Sa parameter. It is also found that the interaction between parameters are of greatest significance on the obtainable surface roughness, though their effects vary greatly depending on the applied levels. This behavior is mainly attributed to the difference in energy absorbed by the powder, however further investigation is still warranted.”
In both up- and down-facing surfaces, SLM 3D printing exhibits what’s called the staircase effect, which can increase their roughness…especially surfaces that face down at less than a 45° angle with respect to the build platform.
“The surface topology of parts produced by SLM are highly dependent on their orientation. This is why, in order to produce parts with good surface quality, down-facing surfaces with angles less than 45° are usually avoided by reorienting the part. Otherwise, there is a need for the building of support structures. However, this in turn results in the increase of process steps, especially the removal of the support could exhibit defects such as burr formation leading to even higher roughness,” the researchers wrote.
This paper looks specifically at the effects of differing build parameters on the surface roughness of down-facing surfaces, in particular when the parameters only change within the plane of the surface facing down and “its immediately adjacent volume.”
“The parameters selected for this research work were the laser power, scan speed and scan spacing. The parameters were varied only for the down-facing surfaces of the build,” the researchers explained. “The remainder of the part was built using the standard build parameters, as recommended by 3D Systems, for a 60 micron layer thickness.”
CAD software was used to design the test pieces so they would have a down-facing surface area of 10 x 20 mm, with a 20 mm depth and overhang inclinations of 25°, 35°, and 45°. The test pieces, which were 3D printed on the 3D Systems ProX DMP 320, were designed so they could measure the down-facing surfaces’ roughness with a profilometer.
The results the researchers published in the paper are for the 3D printed test pieces with a 45° overhang angle. At the lower scanning speed, the experiment showed that the laser power didn’t significantly affect the observed roughness parameters. At a lower laser power of 90W, the roughness parameters only increased a little when the scan spacing went up. The team determined from their results that “increasing the scan spacing results in the decrease of roughness values,” for both the low and high values of scan speed.
“Figure 9 depicts the measured Sa and Sz values for all the test pieces. It is clear that the Sa values over the whole square does not exhibit drastic changes across all the tested sample but on the other hand the Sz values exhibit significant deviations though they have similar Sa values,” the researchers wrote.
“Fig 10 shows 3D topographies of two surfaces that measured with similar Sa values but display very different surface qualities. The variations in the Sz parameter can be attributed to the disturbance of the surface due to the presence of partially melted powder as well as dross formation that results in high peaks and low valleys resulting in non-uniformity.”
The results of the study indicate that, due to its surface non-conformity, the Sz parameter offers more insight than the Sa parameter does into surface quality.
“The presence of partially melted powder and dross formation is the major cause of surface defects within the down-facing surfaces,” the researchers wrote. “Results clearly indicate that for down-facing regions, increasing scan spacing results in lower roughness values, while a higher scan speed increases surface roughness.”
The degree of laser power demonstrated different degrees of effect on the overall surface quality.
“Though relationships begin to arise between parameters, the non-linear behavior and the complex interactions between process parameters add to its unpredictability,” the researchers concluded. “Which makes this process a prime candidate for process modelling and optimization.”
Co-authors of the paper Amal Prashanth Charles, Ahmed Elkaseer, Tobias Müller, Lore Thijs, Maika Torge, V. Hagenmeyer, and Steffen Scholz.